Zirconia Toughened Alumina Beads and Balls, Sintered (Invented for Wet Grinding)
ZTA-W beads & balls are unique products, developed by expert R&D team after several years of research and experiments. We adopt our experienced roll / granulation method for forming this type of products to make it specifically suitable for wet grinding applications. Proved by many comparison wear rate tests, ZTA-W shows 4 - 30 times better in wear resistance than various quality High Alumina ( 90 - 92 % Al2O3 ) grinding media in global market, and its similar density enables this product to substitute High Alumina media very well.
Until now, Zirconia Toughened Alumina Beads & Balls are successfully being used in many modern types of mills, which include vertical mills, horizontal mills, agitated media mills and stirred media mills, such as IsaMill™, Metso Vertimill®, Metso SMD, FLSmidth® VXPmill, OUTOTEC HIGmill® and many conventional ball mills.
Features
Available in big sizes balls up to ∅70 mm, which suits wet-grinding in ball mills
At least 4 times better in wear resistance than “the best” High Alumina ( 90 - 92 % Al2O3 ) grinding media in the world market, proved by many tests
The product's similar density enables it to substitute High Alumina media very well
Superior performance-price ratio saving users' cost
This is the grinding media recommended by us for fine and ultra-fine grinding gold, silver, platinum, lead, copper and zinc sulfide
Main Applications
ZTA-W beads/balls are specifically suitable for wet grinding of following materials in ceramic and mining industry, just name a few:
Ceramic body, glaze and zircon
Gold, silver, platinum, lead, copper and zinc sulfide
Chemical Composition
| Zirconium Oxide ( ZrO2 ) | 2% |
| Silica ( SiO2 ) | 4% |
| Aluminium Oxide ( Al2O3 ) | 90% |
Properties *
| Density ( g/cc ) | 3.65 |
| Bulk density ( kg/l ) | 2.3 |
| Hardness ( HV5 ) | 1230 |
| Mohs' hardness | 9 |
| Breaking load (N) | 800 |
| Color White | white |
Wear Rate
Wet Grinding 0.03 %
Test Condition
a Lab Ball Mill (Jar Mill) Size: 7.6 L, Media Size: 40 mm,
Media Feed: 4 kg (Media Filling Volume =23%),
Water Feed: 4 L, Material Feed: 3 kg Zircon sand,
Mill Speed: 90 rpm,
Grinding Test Time: 24 hrs
Standard Sizes (∅,mm ) *
2.0 - 2.5 2.5 - 3.0 3.0 - 3.5 3.5 - 4.5 4.5 - 5.5
5.5 - 6.5 6.5 - 7.5 7.5 - 8.5 9 - 11 11 - 13
12 - 14 14 - 16 16 - 18 18 - 20
Balls
20 ± 1 26 ± 1.5 32 ± 1.5 35 ± 2 40 ± 2
45 ± 2 52 ± 2 63 ± 2 70 ± 3